Master Models Tooling Paste Epoxy Resin Materials Packing 10kg 15kg 20kgs Product main properties This product is a two-component materials, by automatically output device fast coating model, single coating thickness can be up to 40 mm, reaction put the quantity of heat low, coating and processing when no smell, room temperature curing can be carried out after a day of machining, machining performance is good, good surface effect, material size stability is good Characteristi
-
Dán dụng cụ bằng nhựa Epoxy 50-55D Mật độ 0,5G / Cm 3 Độ cứng Màu hồng cho mô hình chính
50-55D Density 0.5 g/cm 3 Hardness Pink Color Tooling Paste For Master Model APPLICATION: ● Master model ● Manufacturing sample ● Automotive design modeling PHYSICAL PROPERTIES Type Color Mixratio Working time Gel time Cured time LH 5300A (resin) Brown 1 20-30Min 40 Min 24 Hour LH5300B (hardener) White 1 CURED PARAMETER Type LH 5300 A/B Color Brown Density(ISO 1183) 0.50g/cm3 Cured Hardness (ISO 868) 50-55shore D Thermal expansion coefficient (ISO 11359) 55-60 x 10-6K-1
-
Dán công cụ màu hồng có độ cứng 50-60D cho mô hình chính
50-60D Hardness pink Color Tooling Paste fit to Master model APPLICATION: ● Master model ● Manufacturing sample ● Automotive design modeling PHYSICAL PROPERTIES Type Color Mixratio Working time Gel time Cured time LH 0500A (resin) Pink 1 20-30Min 40 Min 24 Hour LH0500B (hardener) White 1 CURED PARAMETER Type LH 0500 A/B Color PINK Density(ISO 1183) 0.5-0.60g/cm3 Cured Hardness (ISO 868) 50-60shore D Thermal expansion coefficient (ISO 11359) 55-60 x 10-6K-1 Thermal deformation
-
65MPa Cường độ 1.1g / Cm3 Dụng cụ dán để tự động kiểm tra vật cố định
Tooling Paste can be processed for auto checking fixture PHYSICAL PROPERTIES Type Color Mix ratio Working time Gel time Cured time LH1000A (resin) Beige 1 40-50 Min 60Min 24 Hour LH1000B (hardener) White 1 CURED PARAMETER Type LH 1000 A/B Color Beige Density(ISO 1183) 1.0-1.1g/cm3 Cured Hardness (ISO 868) 70-75shore D Thermal expansion coefficient (ISO 11359) 50-55 x 10-6K-1 Thermal deformation temperature(ISO 75) 60-65℃ Compressive strength (ISO 604) 60-65 MPa Specifications
-
Keo dán dụng cụ nhựa Epoxy màu be để tạo mô hình ô tô
70-75D Hardness beige Color Tooling Paste fit to Automotive design modeling APPLICATION: ● Master model ● Manufacturing sample ● Automotive design modeling Type Color Mix ratio Working time Gel time Cured time LH1000A (resin) Beige 1 30-40 Min 40 Min 24 Hour LH1000B (hardener) White 1 CURED PARAMETER Type LH1000 A/B Color beige Density(ISO 1183) 1.0-1.1g/cm3 Cured Hardness (ISO 868) 70-75shore D Thermal expansion coefficient (ISO 11359) 55-60 x 10-6K-1 Thermal deformation
-
Độ cứng 70-75D Dán công cụ màu nâu cho mô hình chính
Epoxy Laminating Resin 70-75D Hardness brown Color Tooling Paste fit to Master model APPLICATION: ● Master model ● Manufacturing sample ● Automotive design modeling Type Color Mix ratio Working time Gel time Cured time LH1000A (resin) Light Brown 1 20-30 Min 40 Min 24 Hour LH1000B (hardener) White 1 CURED PARAMETER Type LH1000 A/B Color Brown Density(ISO 1183) 1.0-1.05g/cm3 Cured Hardness (ISO 868) 70-75shore D Thermal expansion coefficient (ISO 11359) 55-60 x 10-6K-1 Thermal
-
Công cụ Làm mẫu Model Paste cho Model Yacht / Model Benchmark Making
Brown Modeling Tooling Paste Epoxy Resin Materials Packing 10kg 15kg 20kg Product operation process Given according to the proportion of fully mixing thoroughly, the same color. Try to avoid to produce bubbles, it is best to use vacuum mixer mixing. Strict control, with a thick layer of a coating is not more than 40 mm;If upset, after waiting for curing the second floor. The after curing processing, performance is better. (after curing: 80 ℃ + 8 h or 3 days) at room
-
Sản xuất khuôn mẫu Dụng cụ Dán nhựa Epoxy Resin Chất lượng Độ chính xác Cao
Beige Modeling Tooling Paste Epoxy Resin Materials Packing 10kg 15kg 20kg Product introduction This product is a two-component epoxy resin imported raw materials, after mixing, apply on the surface of model, after curing on nc machining can be processed into the required model, according to different design requirements for glue, curing content has excellent machining performance, milling, planing, cutting, drilling, and other processing, without a bit wear in the processing,